ARC S1HB
- High Build, Single Coat, Edge-Retentive Barrier Coating
ARC S1HB is a mineral reinforced, amidoamine cured modified epoxy lining for the protection of metallic and cementitious surfaces from corrosive exposures. Its high build, edge-retentive nature provides maximum coverage over hard 90° edges and corners with minimal thinning at the sharp edge.
Product Features
-
- Low VOCs
- 100% solids
- Greater than 70% edge retention
- Provides excellent barrier protection against corrosion and chemical attack
- Provides resistance to erosive flow
- High build (1 – 2 mm/ 40 – 80 mils) coating designed for rough surfaces
- Easily applied by heated plural component spray with brush application for touch-up
- UV sensitive pigment for QC inspection
Technical Data
Applications |
|
---|---|
Dry Temperature Max | 80 °C ( 175 °F ) |
Wet Temperature Max | 52 °C ( 125 °F ) |
Tensile Adhesion | 4400 PSI ( 309 kg/cm2 ) ( 30 Mpa ) ( 400 PSI ) ( 28 kg/cm2 ) ( 2.7 Mpa ) |
Salt fog | 10000 minutes |
Color | Light Gray |
Available Container Sizes |
ARC S1HB: Nominal, based on a 750 µm (30 mil) DFT
Note: Each kit is comprised of two equal size units of Part A and one equal size unit of Part B |
Let's talk
For inquires about products, sales, or requesting a quote, please contact our Sales Office.
Resources
Name | Download | File type | |
---|---|---|---|
|
Technical Bulletin 4: Spark Testing ARC Products (English) | 239 KB |